1. 產品資料

 

AFG00Y（PA66-V0）
Flame Retardant Grade(Non-Phosphorous & Halogen-free)

 

Properties

 

Method

Unit

Values

23℃

23℃-RH50

Physical

Water absorption, 24h in water at 23℃

ISO 62

%

1.7

-

 

Density

ISO 1183-A

g/cm3

1.16

-

 

Moulding shrinkage longitudinal

YC-EP

%

1.3

-

 

Moulding shrinkage transverse

YC-EP

%

2.0

-

Mechanical

Tensile strength

ISO 527

MPa

83

-

 

Nominal elongation at break

ISO 527

%

10.0

-

 

Flexural strength

ISO 178

MPa

118

-

 

Flexural modulus

ISO 178

MPa

3200

-

 

Izod notched impact strength

ISO 180

KJ/㎡

3.8

-

Thermal

Melt temperature

ISO3146-C

℃

263

-

 

Temper of dimensional stability 66psi

ISO 75-1

℃

240

-

 

Temper of dimensional stability 264psi

ISO 75-2

℃

110

-

 

Flammability UL-94 thickness 0.4mm

ISO 1210/UL94

WT/NC

V0

-

 

Flammability UL-94 thickness 1.6mm

ISO 1210/UL94

-

V0

-

 

Flammability UL-94 thickness 3.0mm

ISO 1210/UL94

-

V0

-

 

Glow wire test thickness 1.6mm

IEC 695-2-1

℃

-

-

 

Glow wire test thickness 3.2mm

IEC 695-2-1

℃

-

-

Electrical

Comparative tracking index KC

UL-746A

Volt

0

-

Injection Cylinder Temperature(℃)  250℃­---280℃­

Mold Temperature(℃)              50℃­---100℃­

Roast Temperature(℃)            80℃­---85℃­

Roast Time(hour)                    4h---6h

Identification Code                          <PA66+V0>              UL

 

AFG30Y（PA66+GF30 V0）Flame Retardant Reinforced Grade  

Properties

 

Method

Unit

Values

23℃

23℃-RH50

Physical

Water absorption, 24h in water at 23℃

ISO 62

%

1.6

-

 

Density

ISO 1183-A

g/cm3

1.56

-

 

Moulding shrinkage longitudinal

YC-EP

%

0.3

-

 

Moulding shrinkage transverse

YC-EP

%

0.6

-

Mechanical

Tensile strength

ISO 527

MPa

145

-

 

Nominal elongation at break

ISO 527

%

3.0

-

 

Flexural strength

ISO 178

MPa

240

-

 

Flexural modulus

ISO 178

MPa

8100

-

 

Izod notched impact strength

ISO 180

KJ/㎡

11.0

-

Thermal

Melt temperature

ISO3146-C

℃

265

-

 

Temper of dimensional stability 66psi

ISO 75-1

℃

260

-

 

Temper of dimensional stability 264psi

ISO 75-2

℃

250

-

 

Flammability UL-94 thickness 0.8mm

ISO 1210/UL94

-

V0

-

 

Flammability UL-94 thickness 1.6mm

ISO 1210/UL94

-

V0

-

 

Flammability UL-94 thickness 3.0mm

ISO 1210/UL94

-

V0

-

 

Glow wire test thickness 1.6mm

IEC 695-2-1

℃

960

-

 

Glow wire test thickness 3.2mm

IEC 695-2-1

℃

960

-

Electrical

Comparative tracking index KC

UL-746A

Volt

2

-

Injection Cylinder Temperature(℃)  260℃­---290℃­

Mold Temperature(℃)              80℃­---120℃­

Roast Temperature(℃)            80℃­---85℃­

Roast Time(hour)                    4h---6h

Identification Code                          <PA66+GF25% V0>    

 

<span lang="EN-US" style="FONT-S

 

AG30Y   (PA66+GF30)
Glass Fiber Reinforced Grade

 

Properties

 

Method

Unit

Values

23℃

23℃-RH50

Physical

Water absorption, 24h in water at 23℃

ISO 62

%

1.7

-

 

Density

ISO 1183-A

g/cm3

1.39

-

 

Moulding shrinkage longitudinal

YC-EP

%

0.3

-

 

Moulding shrinkage transverse

YC-EP

%

0.6

-

Mechanical

Tensile strength

ISO 527

MPa

183

126

 

Nominal elongation at break

ISO 527

%

3.0

5.0

 

Flexural strength

ISO 178

MPa

283

215

 

Flexural modulus

ISO 178

MPa

9100

6800

 

Izod notched impact strength

ISO 180

KJ/㎡

13.5

21

Thermal

Melt temperature

ISO3146-C

℃

265

-

 

Temper of dimensional stability 66psi

ISO 75-1

℃

260

-

 

Temper of dimensional stability 264psi

ISO 75-2

℃

250

-

 

Flammability UL-94 thickness 0.8mm

ISO 1210/UL94

-

HB

-

 

Flammability UL-94 thickness 1.6mm

ISO 1210/UL94

-

HB

-

 

Flammability UL-94 thickness 3.0mm

ISO 1210/UL94

-

HB

-

 

Glow wire test thickness 1.6mm

IEC 695-2-1

℃

-

-

 

Glow wire test thickness 3.2mm

IEC 695-2-1

℃

-

-

Electrical

Comparative tracking index KC

UL-746A

Volt

0

-

Injection Cylinder Temperature(℃)  260℃­---290℃­

Mold Temperature(℃)              80℃­---120℃­

Roast Temperature(℃)            80℃­---85℃­

Roast Time(hour)                    4h---6h

Identification Code                          <PA66+GF33% HB>

 

 
AG15Y（PA66+GF15)

Glass Fiber Reinforced Grade  

Properties

 

Method

Unit

Values

23℃

23℃-RH50

Physical

Water absorption, 24h in water at 23℃

ISO 62

%

1.7

-

 

Density

ISO 1183-A

g/cm3

1.25

-

 

Moulding shrinkage longitudinal

YC-EP

%

0.4

-

 

Moulding shrinkage transverse

YC-EP

%

0.9

-

Mechanical

Tensile strength

ISO 527

MPa

125

-

 

Nominal elongation at break

ISO 527

%

2.5

-

 

Flexural strength

ISO 178

MPa

170

-

 

Flexural modulus

ISO 178

MPa

7000

-

 

Izod notched impact strength

ISO 180

KJ/㎡

8.2

-

Thermal

Melt temperature

ISO3146-C

℃

265

-

 

Temper of dimensional stability 66psi

ISO 75-1

℃

260

-

 

Temper of dimensional stability 264psi

ISO 75-2

℃

245

-

 

Flammability UL-94 thickness 0.8mm

ISO 1210/UL94

-

HB

-

 

Flammability UL-94 thickness 1.6mm

ISO 1210/UL94

-

HB

-

 

Flammability UL-94 thickness 3.0mm

ISO 1210/UL94

-

HB

-

 

Glow wire test thickness 1.6mm

IEC 695-2-1

℃

-

-

 

Glow wire test thickness 3.2mm

IEC 695-2-1

℃

-

-

Electrical

Comparative tracking index KC

UL-746A

Volt

0

-

Injection Cylinder Temperature(℃)  260℃­---280℃­

Mold Temperature(℃)              80℃­---120℃­

Roast Temperature(℃)            80℃­---85℃­

Roast Time(hour)                    4h---6h

Identification Code                          <PA66+GF15% HB>

 

 
AG20Y（PA66+GF20）

Glass Fiber Reinforced Grade

 

Properties

 

Method

Unit

Values

23℃

23℃-RH50

Physical

Water absorption, 24h in water at 23℃

ISO 62

%

1.7

-

 

Density

ISO 1183-A

g/cm3

1.25

-

 

Moulding shrinkage longitudinal

YC-EP

%

0.4

-

 

Moulding shrinkage transverse

YC-EP

%

0.9

-

Mechanical

Tensile strength

ISO 527

MPa

125

-

 

Nominal elongation at break

ISO 527

%

2.5

-

 

Flexural strength

ISO 178

MPa

170

-

 

Flexural modulus

ISO 178

MPa

7000

-

 

Izod notched impact strength

ISO 180

KJ/㎡

8.2

-

Thermal

Melt temperature

ISO3146-C

℃

265

-

 

Temper of dimensional stability 66psi

ISO 75-1

℃

260

-

 

Temper of dimensional stability 264psi

ISO 75-2

℃

245

-

 

Flammability UL-94 thickness 0.8mm

ISO 1210/UL94

-

HB

-

 

Flammability UL-94 thickness 1.6mm

ISO 1210/UL94

-

HB

-

 

Flammability UL-94 thickness 3.0mm

ISO 1210/UL94

-

HB

-

 

Glow wire test thickness 1.6mm

IEC 695-2-1

℃

-

-

 

Glow wire test thickness 3.2mm

IEC 695-2-1

℃

-

-

Electrical

Comparative tracking index KC

UL-746A

Volt

0

-

Injection Cylinder Temperature(℃)  260℃­---280℃­

Mold Temperature(℃)              80℃­---120℃­

Roast Temperature(℃)            80℃­---85℃­

Roast Time(hour)                    4h---6h

 

AC30Y（PA66+CF30）Glass Fiber+Carbon Fiber Reinforced Grade

 

Properties

 

Method

Unit

Values

23℃

23℃-RH50

Physical

Water absorption, 24h in water at 23℃

ISO 62

%

1.7

-

 

Density

ISO 1183-A

g/cm3

1.33

-

 

Moulding shrinkage longitudinal

YC-EP

%

0.15

-

 

Moulding shrinkage transverse

YC-EP

%

0.35

-

Mechanical

Tensile strength

ISO 527

MPa

185

-

 

Nominal elongation at break

ISO 527

%

2.5

-

 

Flexural strength

ISO 178

MPa

290

-

 

Flexural modulus

ISO 178

MPa

9400

-

 

Izod notched impact strength

ISO 180

KJ/㎡

13

-

Thermal

Melt temperature

ISO3146-C

℃

--

-

 

Temper of dimensional stability 66psi

ISO 75-1

℃

260

-

 

Temper of dimensional stability 264psi

ISO 75-2

℃

250

-

 

Flammability UL-94 thickness 0.8mm

ISO 1210/UL94

-

HB

-

 

Flammability UL-94 thickness 1.6mm

ISO 1210/UL94

-

HB

-

 

Flammability UL-94 thickness 3.0mm

ISO 1210/UL94

-

HB

-

 

Glow wire test thickness 1.6mm

IEC 695-2-1

℃

-

-

 

Glow wire test thickness 3.2mm

IEC 695-2-1

℃

-

-

Electrical

Comparative tracking index KC

UL-746A

Volt

-

-

Injection Cylinder Temperature(℃)  260℃­---305℃­

Mold Temperature(℃)              80℃­---120℃­

Roast Temperature(℃)            80℃­---85℃­

Roast Time(hour)                    4h---6h

Identification Code                          <PA66+GF25%+CF5% HB>

   

S94（PPS+GF40 V0）  Glass Fiber Reinforced Grade

Properties

 

Method

Unit

Values

 

23℃

 

Physical

Water absorption, 24h in water at 23℃

ISO 62

%

0.5

 

 

Density

ISO 1183-A

g/cm3

1.65

 

 

Moulding shrinkage longitudinal

YC-EP

%

0.1

 

 

Moulding shrinkage transverse

YC-EP

%

0.25

 

Mechanical

Tensile strength

ISO 527

MPa

170

 

 

Nominal elongation at break

ISO 527

%

2.5

 

 

Flexural strength

ISO 178

MPa

275

 

 

Flexural modulus

ISO 178

MPa

13000

 

 

Izod notched impact strength

ISO 180

KJ/㎡

12

 

Thermal

Melt temperature

ISO3146-C

℃

293

 

 

Temper of dimensional stability 66psi

ISO 75-1

℃

285

 

 

Temper of dimensional stability 264psi

ISO 75-2

℃

268

 

 

Flammability UL-94 thickness 0.8mm

ISO 1210/UL94

-

V0

 

 

Flammability UL-94 thickness 1.6mm

ISO 1210/UL94

-

V0

 

 

Flammability UL-94 thickness 3.0mm

ISO 1210/UL94

-

V0

 

 

Glow wire test thickness 1.6mm

IEC 695-2-1

℃

-

 

 

Glow wire test thickness 3.2mm

IEC 695-2-1

℃

-

 

Electrical

Comparative tracking index KC

UL-746A

Volt

-

 

Injection Cylinder Temperature(℃)                                       285℃­---310℃­

Mold Temperature(℃)                                                    80℃­---120℃­

Roast Temperature(℃)                                                  100℃­---140℃­

Roast Time(hour)                                                          4h---6h

     

 
 
TFG30Y（PBT+GF30V0）

Flame Retardant Reinforced Grade

Properties

 

Method

Unit

Values

 
 

23℃

 

Physical

Water absorption, 24h in water at 23℃

ISO 62

%

 

 

 

Density

ISO 1183-A

g/cm3

0.3

 

 

Moulding shrinkage longitudinal

YC-EP

%

1.62

 

 

Moulding shrinkage transverse

YC-EP

%

0.2

 

Mechanical

Tensile strength

ISO 527

MPa

0.4

 

 

Nominal elongation at break

ISO 527

%

125

 

 

Flexural strength

ISO 178

MPa

2.5

 

 

Flexural modulus

ISO 178

MPa

160

 

 

Izod notched impact strength

ISO 180

KJ/㎡

8100

 

Thermal

Melt temperature

ISO3146-C

℃

9.0

 

 

Temper of dimensional stability 66psi

ISO 75-1

℃

--

 

 

Temper of dimensional stability 264psi

ISO 75-2

℃

220

 

 

Flammability UL-94 thickness 0.8mm

ISO 1210/UL94

-

210

 

 

Flammability UL-94 thickness 1.6mm

ISO 1210/UL94

-

V0

 

 

Flammability UL-94 thickness 3.0mm

ISO 1210/UL94

-

V0

 

 

Glow wire test thickness 1.6mm

IEC 695-2-1

℃

V0

 

 

Glow wire test thickness 3.2mm

IEC 695-2-1

℃

--

 

Electrical

Comparative tracking index KC

UL-746A

Volt

--

 

Injection Cylinder Temperature(℃)                                            225℃­---265℃­

Roast Temperature(℃)                                                      80℃­---85℃­

Roast Time(hour)                                                              4h---6h

 

  
           

 
Identification Code                          <PBT+GF30% V0>
 
     EFG30Y（PET+GF30 V0）Glass Fiber Reinforced Grade

Properties

 

Method

Unit

Values

 

23℃

 

Physical

Water absorption, 24h in water at 23℃

ISO 62

%

0.1

 

 

Density

ISO 1183-A

g/cm3

1.61

 

 

Moulding shrinkage longitudinal

YC-EP

%

0.2

 

 

Moulding shrinkage transverse

YC-EP

%

0.8

 

Mechanical

Tensile strength

ISO 527

MPa

140

 

 

Nominal elongation at break

ISO 527

%

1.4

 

 

Flexural strength

ISO 178

MPa

200

 

 

Flexural modulus

ISO 178

MPa

11000

 

 

Izod notched impact strength

ISO 180

KJ/㎡

7

 

Thermal

Melt temperature

ISO3146-C

℃

253

 

 

Temper of dimensional stability 66psi

ISO 75-1

℃

255

 

 

Temper of dimensional stability 264psi

ISO 75-2

℃

225

 

 

Flammability UL-94 thickness 0.8mm

ISO 1210/UL94

-

V0

 

 

Flammability UL-94 thickness 1.6mm

ISO 1210/UL94

-

V0

 

 

Flammability UL-94 thickness 3.0mm

ISO 1210/UL94

-

V0

 

 

Glow wire test thickness 1.6mm

IEC 695-2-1

℃

-

 

 

Glow wire test thickness 3.2mm

IEC 695-2-1

℃

-

 

Electrical

Comparative tracking index KC

UL-746A

Volt

-

 

Injection Cylinder Temperature(℃)                                       195℃­---250℃­

Mold Temperature(℃)                                                    80℃­---90℃­

Roast Temperature(℃)                                                  100℃­---100℃­

Roast Time(hour)                                                          4h---6h

Identification Code                          <PET+GF30% V0>

 

AG30Y物性
 
物理性能              
物性項目   測定標準 測定條件   單位   額定值
比重   GB1033     g/㎤   1.36
成型收縮率   GB15585     %   0.2-0.4
機械性能              
物性項目   測定標準 測定條件   單位   額定值
拉伸強度   GB1040-92     MPA   170
拉伸斷裂伸長率   GB1040-92     %   3
拉伸模量   GB1040-91     MPA   9000
彎曲強度   GB9341-88     MPA   230
彎曲模量   GB9342-88     MPA   8500
簡支梁衝擊強度   GB9342-88     KJ/㎡   16
熱性能              
物性項目   測定標準 測定條件   單位   額定值
負荷熱變形溫度   GB-1634     ℃   245